Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system

Shafiq, N. and Nuruddin, F (2010) Degree of hydration and compressive strength of conditioned samples made of normal and blended cement system. [Citation Index Journal]

[thumbnail of KSCE-S-10-00176.pdf] PDF
KSCE-S-10-00176.pdf
Restricted to Registered users only

Download (560kB)

Abstract

Abstract: In this paper; results of the degree of hydration of the pastes and the compressive strength of
the 50 mm cubes prepared with the 100% cement and fly ash blended cement was determined. 24
hours after casting mortar cubes and the paste samples were cured for 28 days in the fog room. After
28 days curing; a set of 3 cubes and a paste sample was dried in the 100%, 75%, 65%, 40% and 12%
ambient relative humidity at the constant temperature of 27oC. Drying conditions showed significant
affects on the compressive strength and the degree of hydration. Highest compressive strength of 70
MPa was measured of mortar cubes dried in 100% RH; similarly 97% degree of hydration was
determined for 100% cement samples dried in the 100% RH. For mortar cubes dried in 12% RH, the
compressive strength was measured between 47 and 53 MPa. The similar paste samples showed the
maximum degree of hydration as 81%.

Item Type: Citation Index Journal
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Dr Nasir Shafiq
Date Deposited: 10 Nov 2010 08:43
Last Modified: 19 Jan 2017 08:24
URI: http://scholars.utp.edu.my/id/eprint/2964

Actions (login required)

View Item
View Item