Improved critical current density in Zn doped YBCO single crystals

Manzoor, Hussain and Koki, Takita (2010) Improved critical current density in Zn doped YBCO single crystals. PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS , 470 (4 ). 291-294 . ISSN 0921-4534

[thumbnail of SAMPLE_PAPER_PDF.pdf] PDF
SAMPLE_PAPER_PDF.pdf
Restricted to Registered users only

Download (12kB)
Official URL: http://apps.isiknowledge.com/full_record.do?produc...

Abstract

Magnetic measurements were made using pure YBCO and Zn doped YBa2(Cu1-xZnx)(3)O7-sigma Single crystals with Zn concentration of 0 5%, 1 5%, 3 0% and 4 3% The magnetic hysteresis loops for these samples were measured in the temperature range 0 1 <= T/T-c <= 0 96 under magnetic fields of 5 T using SQUID. It was found that the critical current density J(c) increased for low Zn content samples up to 3% Zn concentration compared to pure YBCO sample and decreased for the higher Zn content samples These values varied consistently when compared at magnetic fields of 1 T and 3 T Moreover Zn doped samples showed significant values of J(c) in the temperature range of 0.7-0.97(c), close to critical temperature compared to pure YBCO sample. The irreversibility field H-irr was also enhanced in this temperature range showing consistent decrease with increase of Zn concentration. The peak field H-p above H-c1 and irreversibility field H-irr, both show power law dependence of the form H = m(1)(1 - T/T-c)(m2) in the temperature range of 0 75-0.96T(c). The values of parameter m(2) increased from 1 44 to 1.95 for the samples up to 3% Zn content and decreased to 1.37 for higher Zn contents The ratio H-irr/H-p was found to be 3-4 for the lower Zn content samples and was 7-8 for the sample with high Zn content indicating more disorder for higher Zn content samples The region between peak field H-p and irreversibility field H-irr was broadened with the increase of Zn concentration. The strong effect of Zn substitution in modifying behavior of these samples even at elevated temperatures is possibly due to the changes in the anisotropy of our samples with the increase of Zn concentration and also due to the locally induced changes in magnetic moments by Zn substitution (C) 2010 Published by Elsevier B.V.

Item Type: Article
Impact Factor: Cites in 2009 to articles published in: 2008 = 448 Number of articles published in: 2008 = 515 2007 = 739 2007 = 1126 Sum: 1187 Sum: 1641 Calculation: Cites to recent articles 1187 = 0.723 Number of recent articles 1641
Uncontrolled Keywords: Physics, Applied
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering
Departments / MOR / COE: Departments > Electrical & Electronic Engineering
Depositing User: Mr Helmi Iskandar Suito
Date Deposited: 23 Jun 2010 12:58
Last Modified: 19 Jan 2017 08:24
URI: http://scholars.utp.edu.my/id/eprint/2356

Actions (login required)

View Item
View Item